4Cr5MoSiV1 steel sheet
COLD rolling
other material M2(w6), M35, D2( cr12mov). SKD11
Port: ningbo or shanghai
Minimum Order Quantity: 2 Ton/Tons
Supply Ability: 300 Ton/Tons per Month
Payment Terms: L/C,D/A,D/P,T/T
Contact SupplierPackaging Detail: suitable for export
Delivery Detail: 6-8weeks
4Cr5MoSiV1 steel sheet
hss & Alloy steel sheet
Specification: Hot-rolled steel sheet Thickness 2.5-10.5mm
Width 800mm
Length 1500-2000mm
Cold -rolled steel sheet Thickness 1.0-2.5mm
Width 750mm
Length 1500-2000mm
Delivery Condition: Annealed hardness HB≤255
Package: Suitable for export
The detailed HSS material we could offer:
1. W6Mo5Cr4V2 (GB), it is similar to M2( ASTM), S6-5-2(DIN), SKH51(JIS)
Chemical Composition: C 0.85, Si 0.38, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10, W 6.00, Mo 4.80 V 1.85
Annealed Hardness: HB≤255
Heat treatment temp: Hardening 1210-1230 Temperings 550
Secondary 63-65 HRC
Application: Be used widely in making all kinds of knives and durable cold working molds
2. W6Mo5Cr4V2Co5 (GB), it is similar to M35( ASTM), 1.3243(DIN), SKH35(JIS)
Chemical Composition: C 0.93, Si 0.38, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10, W 6.30, Mo 4.80 V 1.85, Co 5.00
Annealed Hardness: HB≤269
Heat treatment temp: Hardening 1200-1220 Temperings 550
Secondary 64-67 HRC
Application: Steel for difficult and hi-speed cutting blades, blades which lay particular on durable
3. W2Mo9Cr4VCo8 (GB), it is similar to M42 ( ASTM), 1.3247(DIN), SKH59(JIS)
Chemical Composition: C 1.10, Si 0.55, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10, W 1.50, Mo 9.50 V 1.05, Co 8.00
Annealed Hardness: HB≤269
Heat treatment temp: Hardening 1210-1230 Temperings 550
Secondary 65-67 HRC
Application: Steel for difficult and hi-speed cutting blades, blades which lay particular on durable
4. W18Cr4V (GB), it is similar to T1 ( ASTM), 1.3355(DIN), SKH2(JIS)
Chemical Composition: C 0.75, Si 0.35, Mn 0.35, P≤0.030, S≤0.030, Cr 4.05, W18, V 1.10
Annealed Hardness: HB≤255
Heat treatment temp: Hardening 1270-1285 Temperings 560
Secondary 62-65 HRC
Application: Steel for common cutting blades
5. W9Mo3Cr4V (GB)
Chemical Composition: C 0.83, Si 0.35, Mn 0.35, P≤0.030, S≤0.030, Cr 4.05, W 8.90, Mo 2.90 V 1.45
Annealed Hardness: HB≤255
Heat treatment temp: Hardening 1220-1240 Temperings 550
Secondary 63-65 HRC
Application: Chinese material, similar capability to M2
6. W6Mo5Cr4V2 Co(GB), it is equal to M2 modify ( ASTM)
Chemical Composition: C 0.80, Si 0.38, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10, W 5.40, Mo 4.80 V 2.10, Co≤0.5
Annealed Hardness: HB≤255
Heat treatment temp: Hardening 1210-1230 Temperings 550
Secondary 62-64 HRC
Application: Better toughness than M2
The detailed DIE STEEL material we could offer:
1. Cr12Mo1V1(GB), it is similar to D2( ASTM), 1.2379(DIN), SKD11(JIS)
Chemical Composition: C 1.50, Si 0.35, Mn 0.35, P≤0.030, S≤0.030, Cr 12.10, W ≤0.40,
Mo 0.85 V 0.6
Annealed Hardness: HB≤255
Heat treatment temp: Hardening 1010-1050 Temperings 200 550
Secondary 62-63 HRC
Application: Steel for pressing mold, cutting knives, or mold, thread rolling dies and ceramic mold in bulk production
2. Cr12MoV (GB), it is similar to 1.2601(DIN), SKD11(JIS)
Chemical Composition: C 1.60, Si 0.35, Mn 0.35, P≤0.030, S≤0.030, Cr 12.00, Mo 0.50 V 0.20
Annealed Hardness: HB≤255
Heat treatment temp: Hardening 1000-1020 Temperings 200 550
Secondary 62-63 HRC
Application: Steel for pressing mold, cutting knives, or mold, thread rolling dies and ceramic mold in bulk production